Ladle magnesia carbon brick is an alkaline refractory material with magnesia content above 90% and periclase as the main crystal phase. Generally, it can be divided into two categories: sintered magnesia bricks (also known as fired magnesia bricks) and chemically bonded magnesia bricks (also known as unfired magnesia bricks). Magnesia carbon brick manufacturers, magnesia bricks with high purity and firing temperature are called direct bonded magnesia bricks due to the direct contact of periclase grains; bricks made of fused magnesia as raw materials are called fused combined magnesia bricks . Generally, it can be divided into two categories: sintered magnesia bricks (also known as fired magnesia bricks) and chemically bonded magnesia bricks (also known as unfired magnesia bricks). Magnesia bricks with high purity and high firing temperature are called direct bonded magnesia bricks due to the direct contact of periclase crystal grains; bricks made of fused magnesia as raw materials are called fused combined magnesia bricks. Aluminum Magnesium Carbon Brick
Ladle magnesia carbon brick
Converter magnesia carbon bricks have high refractoriness, good alkali slag resistance, high load softening starting temperature, but poor thermal shock resistance. Sintered magnesia bricks are made of brick magnesia bricks. After being crushed, batched, kneaded and shaped, they are fired at a high temperature of 1550 to 1600°C. The firing temperature of high-purity products is above 1750°C. Non-cast magnesia bricks are made by adding appropriate chemical binders to magnesia, mixing, molding and drying. Based on the experience of producing magnesia bricks, magnesia brick company, in order to make the kiln lining material give full play to its effectiveness, to ensure the life cycle of the kiln lining material